Blend Felt ( PPS + PTFE )

We Value Your Feedback !

CASE

产品名称

Blend Felt ( PPS + PTFE )

Serial number
Affiliate classification
Product description

PPS + PTFE Blend Felt

The compound filter materials are the latest developed products, for achieving comprehensive good performance to resist high-temperature, wearing, folding broken, corrosion, and get higher strength on tension and felt fiber stripping.

The advantage of fiber blend fabrication, is especially important with Glass Fiber felt, to rapidly improve the processing performance: no or minimize the damage to the filtration felt during processing.

With various blending solution, & treatment to the surface, the felt products can combine various features in one: clean up the dust, water & oil resistance, anti-statics. Working temperature ranges: 180℃-260℃.

It is widely used in metallurgical industry, cement & nonferrous metal industry, chemical industry, Building material industry, power industry, etc.

Description

Products Code & Data

PPS +PTFE Blended Felt
PFTE Emulsion Impregnated

N-PPS+PTFE)/PTFE-650G / PTFE-EI
30% Super fine PPS fabric on surface
PTFE-EI : PFTE Emulsion Impregnated

Weight per Square Meter (Normal)

650 G

Material (Fiber/Scrim)

(PPS50%+PTFE50%)/PTFE

Thickness

1.9~2.1 mm

Air permeability

12~16 M3/M2.Min@200Pa

Warp Tensile Strength

900N/5×20cm

Weft Tensile Strength

1200N/5×20cm

Warp Elongation

35%/(5×20cm)

Weft Elongation

50%/(5×20cm)

Continuous service Temperature

< 200℃

Instant (<10Min.) Temperature bears

< 220℃

 Liner Shrinkage@130 ℃

MD<1.5%, XD<1%

 Mechanical Finish

Heat Setting, Calendering

 Chemical Finish

/

 Mullen PSI

/

 Water Repellent

/

 Surface Electric-Resistance

/

Special Surface or Deep Treatment
(In case client specially request to)

PTFE Membrane Laminated (PTFE-ML),
or PFTE Emulsion  Impregnated (PTFE-EI)

Other Customize Requests

Acceptable depends on MOQ.

Corresponding parameter set not found, please add it in property template of background